Heat Shrink 2X Tubing (Green-Yellow)

MATERIAL:

POLYOLEFIN (CROSSLINKED)

FEATURE:

FLAME RETARDANT

VOLTAGE:

600 V

RATIO:

2：1

WALL TYPE:

STANDARD

SHRINK TEMP:

100°C

WORK TEMP:

-55°C-125°C

STANDARD:

UL 224 125°C

UL FILE:

E197895

EASE CODE

AS SUPPLIED (mm)

AFTER RECOVERY (mm)

QUANTITY/ CTN

Inside

Wall

Inside

Wall

Diameter (D)

Thickness (T)

Diameter (D)

Thickness (T)

(D)

(T)

(d)

(t)

mm

inch

mm

mm

inch

mm

m

HS-SW-1.2/0.6-GY

1.2

3/64

0.18

0.6

3/128

0.36

3900

HS-SW-1.6/0.8-GY

1.6

1/16

0.18

0.8

1/32

0.36

3900

HS-SW-2.4/1.2-GY

2.4

3/32

0.20

1.2

3/64

0.42

1950

HS-SW-3.2/1.6-GY

3.2

1/8

0.22

1.6

1/16

0.46

1500

HS-SW-4.8/2.4-GY

4.8

3/16

0.23

2.4

3/32

0.46

750

HS-SW-6.4/3.2-GY

6.4

1/4

0.25

3.2

1/8

0.55

600

HS-SW-9.5/4.7-GY

9.5

3/8

0.28

4.7

3/16

0.58

780

HS-SW-12.7/6.4-GY

12.7

1/2

0.28

6.4

1/4

0.58

600

HS-SW-16/8-GY

16

5/8

0.28

8

5/16

0.58

600

HS-SW-19.1/9.5-GY

19.1

3/4

0.32

9.5

3/8

0.68

480

HS-SW-25.4/12.7-GY

25.4

1

0.40

12.7

1/2

0.78

300

HS-SW-32/16-GY

32

1-1/4

0.40

16

5/8

0.82

300

Tensile Strength

≥10.4MPa

Tensile Strength After Aging

≥7.3MPa

158°C 168 hrs

Elongation

≥200%

Elongation After Aging

≥100%

134°C 60 days

Longitudinal Change

-5%~+5%

Radial Shrinking Ratio

≥50%

Flammability

VW-1

Dielectric Strength

≥15kV/mm

Volume Resistivity

≥1*10¹² Ω -cm

Corrosion

No Corrosion

Concentricity

≥70%

Copper Stability

≥100%